Far infrared ray ceramic heater infrared heating

              Infrared heating     

Specifications of   Infrared heating :

Infrared heating   
-Material:ceramic for body 
-Used in chemical industry 
-High quality & best price

Infrared heating

 Embedding type ceramic far infrared radiated elements apply glaze with high radiance,ceramic with good heat and shock property as base,and are sintered once by nichrome wire.

 Components of Infrared heating  :

1.Base body:made of ceramic material with good heat shock property.

2.Heating nature:sintered by high quality nichrome wire.

3.Glaze:composed of metal oxide material with good far infrared radiated property.

4. Put right amount of additive and improve radiant intensity and strengthen adaptability of glaze billet

Main technical parameter and property of Infrared heating :

1.Radiated characteristic: the tiptop single color of radiance of element can reach 0.9

2.Time of heating response: from room temperature to surface temperature of radiated plate, the fixed time will not exceed 20 minutes.

3.Cold and hot resistance: the base body is heated to 800 C and put in cold water repeatly for many times and no cracking. After cold and hot mutual change test for five times, no peel and no craze.

4. The radiated element is heated after electrifying to rating power and immerged into cold water after interruption of power supply for forty times without damage.

5.Good chemical stability; strong causticity-resistance; perfect oxidation-resistance

6.The heating damage of non radiated surface is small.

7. Resistance in common temperature: 10^12 ohm ^0cm

8.Uneven degree for radiated surface temperature:≤15%

9. Rupture strength for base body: 440Kg/cm2

10.Tolerance of power: ≤5% at rating working voltage

11.Cold state insulated resistance 500V tramegger>2 mΩ

12.Thermal state insulated resistance: 500V tramegger>5 mΩ

13.Using life span: >3000 hours

14.The effect of energy saving is obvious, increasing 10-25% compared with silicon carbide element

15. The life span can prolong more than a few times compared with silicon carbide element.